Apparatus and method for detecting surface defects on a workpiece such as a rolled/drawn metal bar

ABSTRACT

The present invention is directed to solving the problems associated with the detection of surface defects on metal bars as well as the problems associated with applying metal flat inspection systems to metal bars for non-destructive surface defects detection. A specially designed imaging system, which is comprised of a computing unit, line lights and high data rate line scan cameras, is developed for the aforementioned purpose. The target application is the metal bars (1) that have a circumference/cross-section-area ratio equal to or smaller than 4.25 when the cross section area is unity for the given shape, (2) whose cross-sections are round, oval, or in the shape of a polygon, and (3) are manufactured by mechanically cross-section reduction processes. The said metal can be steel, stainless steel, aluminum, copper, bronze, titanium, nickel, and so forth, and/or their alloys. The said metal bars can be at the temperature when they are being manufactured. A removable cassette includes various mirrors. A protection tube isolates the moving metal bar from the line light assembly and image acquisition camera. A contaminant reduction mechanism applies a vacuum to remove airborne contaminants.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. application Ser. No. 11/931,339 filed on Oct. 31, 2007, now allowed, which in turn is a (1) continuation under 35 U.S.C. § 120 and §§ 365(c) of PCT International Application No. PCT/2006/029884 filed Jul. 31, 2006 entitled “AN APPARATUS AND METHOD FOR DETECTING SURFACE DEFECTS ON A WORKPIECE SUCH AS A ROLLED/DRAWN METAL BAR” (attorney Docket No. 63,937-0146), now abandoned as to the United States, which in turn claims the benefit of U.S. application Ser. No. 11/194,985 filed on Aug. 2, 2005, now U.S. Pat. No. 7,324,681, the disclosures of which are each incorporated by reference in their entirety; and (2) a continuation-in-part (CIP) of U.S. application Ser. No. 11/194,985 filed on Aug. 2, 2005 entitled “AN APPARATUS AND METHOD FOR DETECTING SURFACE DEFECTS ON A WORKPIECE SUCH AS A ROLLED/DRAWN BAR” (attorney docket no. 63,937-0142), now U.S. Pat. No. 7,324,681, U.S. application Ser. No. 11/194,985 in turn being a continuation-in-part (CIP) of U.S. application Ser. No. 10/331,050 filed on Dec. 27, 2002 entitled “APPARATUS AND METHOD FOR DETECTING SURFACE DEFECTS ON A WORKPIECE SUCH AS A ROLLED/DRAWN METAL BAR” (attorney Docket No. 63,937-0125), now U.S. Pat. No. 6,950,546, which in turn claims the benefit of U.S. Provisional Application No. 60/430,549 filed Dec. 3, 2002 (attorney Docket No. 63,937-0124), the disclosures of which are each hereby incorporated herein by reference in their entirety.

STATEMENT REGARDING FEDERALLY FUNDED RESEARCH

This invention or portions thereof was made with United States government support under Cooperative Agreement No. 70NANBOH3014 awarded by the National Institute of Standards and Technology (NIST). The United States government has certain rights in the invention.

BACKGROUND OF THE INVENTION

1. Related Field

The present invention relates generally to an imaging system that can image the surface details of a workpiece, such as a rolled/drawn metal bar.

2. Description of the Related Art

It is known to produce a metal bar by a mechanical process such as rolling or drawing. Such metal bar is different than a metal slab, bloom, or strip (hereafter referenced as Metal Flat) in that the cross section of such a bar has a smaller circumference/cross-section-area ratio such that the bar may rotate/twist about a longitudinal axis while moving forward longitudinally. For example, the bar shapes shown in FIG. 2 have a ratio of circumference to cross-sectional-area that is equal to or smaller than 4.25 when the cross sectional area is unity for the given shape. The shape, when taken in cross section, of such a metal bar may be a round shape (item 102), an oval shape (item 104), or a polygonal shape, as shown as a hexagon (item 106), octagon (item 108) or a square (item 110) in FIG. 2. Furthermore, such a metal bar is substantial in length. The length to circumference ratio is typically over 10 and the length to cross-section critical dimension (such as the diameter of a round bar or the side width a square bar) is over 30. A metal bar of this type is typically referred to as “long products” rather than “flat products” in the related industries. Rolling, drawing, extrusion and the like, as used in this disclosure and hereafter referenced as a Reducing Process, describe the ways for reducing the cross sectional dimensions of the metal workpiece through mechanical contact of the applicable tools, such as rollers and drawing dies, and the workpiece. These Reducing Processes are generally continuous, or substantially continuous, in nature.

In the metal production industry, the presence or absence of surface defects is a relevant criterion upon which assessments of the metal products are made. For instance, surface defects account for half of the external rejects (i.e., rejected by the customer) for the steel bar and rod industry. However, the conventional art provides no reliable means to detect such defects. There are several challenges that conventional inspection approaches have been unable to overcome.

First, in the case where inspection occurs while the metal bar products are “hot,” the temperature can be as high as 1,100° C., preventing the use of many inspection technologies. Second, the traveling speed of such a metal bar along its longitudinal axis as described above can be, presently, as fast as 100 m/s, several times faster than the speed of the fastest metal strip and nearly 100 times faster than a metal slab or bloom. Further, speed increases are expected in the near future in the range of 150 m/s to 200 m/s. Conventional inspection approaches simply cannot accommodate such high traveling speeds. Third, a high temperature metal bar such as described above is typically confined in a sectional conduit so that the bar will not cobble. Cobbling is an incident wherein a hot, high speed metal bar runs freely outside the conduit. The space, therefore, for any inspection device is extremely limited. Last, the length of such a metal bar, together with the fact of its longitudinal motion, makes the handling of the bar difficult and costly.

While it is known to apply various imaging approaches to the inspection of cast or rolled Metal Flats in line, visible light imaging technologies have heretofore not been used in in-line Long Products (i.e., metal bar with a substantial length) inspection. Conventional imaging systems are not believed capable for use in inspecting metal bars and the like because the geometry of the metal bars invalidate the illumination and imaging designs that are used to enhance/capture defects on flat surfaces. FIG. 4 illustrates the differences of applying illumination and of capturing images on a flat workpiece (i.e., image line 318 converges on illumination line on flat 316) versus a round workpiece. As to the non-flat workpiece, the freedom in optical alignment and optical working ranges disappears when the object of interest does not have a flat surface. For instance, the image line 18 and the illumination line 18′ may not overlap if the light or the camera is tilted, as shown in exemplary fashion in FIG. 4. One prior art approach employs the use of area cameras to inspect the bar surfaces. However, it requires that the bar be stationary during imaging. Another prior art approach employs the use of line scan cameras, yet requiring the bar to spin for the scanning due to its flat lighting design. In order to cope with the high longitudinal traveling speed, photo-sensitive diodes, instead of imaging sensors, are used in yet another prior art. The use of photo-sensitive diodes limits the capability of detection to short, transverse defects on the bar surface. This approach is incapable of detecting long, thin defects such as seams on a steel bar.

To avoid the lighting issue, use of infrared (IR) imaging devices is reported. In this approach, IR cameras are used to capture the self-radiated light from the long products. This approach is limited to the surface defect detection solely based on surface temperature. It is known that surface voids of a hot object appear to be hotter than their neighborhoods due to the cavity theory, even though these voids are at the same temperature as their neighborhoods. This approach is further limited to its detection capability because of the focusing resolution limit of IR radiation. It is known to those skilled in the art that the optical focusing resolution is inversely proportional to the wavelength of the radiation. Typically IR cameras are nearly 10 times more expensive than a visible one and IR cameras are limited in their imaging speed due to the sensor property. As a result, this approach would not be able to accommodate the speed of today's long products.

Temperature also makes the long products different to their flat counterpart. Metal bars typically are at a higher temperature than Metal Flats. Heat dissipation of an object is proportional to the area exposed to the cooling media, such as ambient air or water spray. The area of a Metal Flat is several times larger than that of a metal bar, assuming both the flat and the bar are made of the same material and both have the same longitudinal unit density and cross section area.

It is, however, known to employ imaging-based instruments for bar gauge measurement/control (shadow measurement), bar existence/presence, and bar traveling speed measurement in the Reducing Process.

It is also known to employ electromagnetic devices, such as eddy current-based instruments, in the assessment of long products. Eddy-current based sensing systems are used for the detection of surface imperfections in the Reducing Process for in-line inspection. This approach has a high response rate, able to work in a high throughput production line environment (e.g., one kilometer of hot steel bars per minute). However, this approach has several drawbacks. First, it must be very close to the hot surface (typically less than 2.5 mm). Accordingly, it is vibration sensitive and temperature sensitive. Moreover, it is not quantitative in the sense that it is NOT able to describe the nature of the detected defect. Finally, eddy-current approaches are incapable of detecting certain types of defects. As a result, the inspection outcome from eddy current devices is not used by the metal industry for a deterministic judgment on the quality of a specific product. Rather, the output of eddy current-based instruments is only used for qualitative analysis, such as “this batch of steel bars is generally worse than the batch produced last week,” in the Reducing Process for process control purposes, for example, only.

Another approach attempted in the art employs ultrasonic sensing. This is an approach to replace the eddy current sensors with ultrasonic ones. However, many of the restrictions associated with eddy current-based instruments, such as the short working distance, apply with equal force.

Other inspection technologies used in the art include magnetic penetrant, circumflux, and infrared imaging with induction heating. The use of these technologies, however, is restricted. First, these techniques can only be used on “cold” metal bars. That is, these technologies cannot be used for in-line inspection during or shortly after hot rolling applications. Also, the metal bars must be descaled before inspection. In addition, the use of magnetic penetrant is messy and cumbersome. This process typically relies on human observation with ultra violet illumination, instead of automatic imaging and detection. The circumflux device is an eddy-current based unit, designed with a rotating detection head. Such rotating mechanism limits the application of this device in metal bar inspection with high traveling speeds, typically used at about 3 m/s. Such device is also expensive due to the moving sensing head design. The combination of induction heating and infrared imaging is based on the fact that induction current is only formed on the surface of the metal bar, and the surface defects on the metal bar will result in higher electrical resistance. Therefore, the spots with surface defects will heat up faster than other areas. There are issues associated with this approach in that (a) such faster heat up is a transient effect and thus timing (time to take images) is very critical; and (b) infrared sensors are not available for very high data rates and therefore cannot support metal bars with high traveling speed.

Of course, inspection is possible after manufacture of the metal bars. However, post-manufacturing inspection often is not possible because the product is so long and coiled up, making the bar surfaces not accessible for cold inspection technologies.

Currently, real-time inspection of metal bars manufactured with Reducing Processes is very limited. Metal bars are generally shipped from the manufacturer to the customer even if defective signals are posted by a conventional in-line eddy current inspection system. Customer complaints may therefore appear 3 to 6 months later due to surface defects on the metal bar products that are not immediately apparent to the customer. Such complaints cost the metal bar suppliers (i.e., manufacturers). The metal bar suppliers will either refund the customers for the entire coil/batch or cost share the expenses of additional labor to inspect the parts made out of the metal bar coil/batch.

There is therefore a need for an apparatus and method to minimize or eliminate one or more of the problems set forth above.

SUMMARY OF THE INVENTION

It is one object of the present invention to overcome one or more of the aforementioned problems associated with conventional approaches for an imaging-based apparatus suitable to be used in-line or off-line to detect surface defects on rolled/drawn metal bars.

The present invention is directed to solving one or more of the problems associated with conventional metal bar inspection systems as well as problems associated with applying metal flat inspection systems to metal bars for non-destructive inspection of surface defects on metal bars through the use of an imaging system.

One advantage of the present invention is that it may be effectively employed in the production of metal bars with the aforementioned characteristics, namely, those that may be at a manufacturing temperature, perhaps even hot enough to produce self-emitted radiation, as well as those subject to rotation relative to a longitudinal axis and may potentially be traveling at a very high speed. Others advantages of the present invention include (i) effectively employed to image and detect defects on non-flat surfaces; (ii) use for inspecting metal bars regardless of its temperature; (iii) use for inspecting metal bars traveling at speeds at or faster than 100 m/s; (iv) providing an increased working distance to the metal bar surface, thus minimizing or eliminating the problems set forth in the Background for eddy-current based instruments; (v) providing an output comprising quantitative data with verifiable defective site images; (vi) inspection of the workpiece even before the scale forms on its surface; (vii) suitable for use in inspection at any stage (between the reducing stands or at the end of the line) in the reducing process, not affected by or relying upon transient effects; (viii) providing real-time or near real-time surface quality information; (ix) providing a system absent of any moving sensing heads, thus minimizing or eliminating the problems of moving components set forth in the Background; (x) providing a system needing only very small gap (less than 50 mm) capable of operating between metal bar guiding conduit sections; and (xi) requiring no additional bar handling mechanisms/apparatuses However, an apparatus and/or method need not have every one of the foregoing advantages, or even a majority of them. The invention is limited only by the appended claims.

A system is provided for imaging an elongate bar extending along a longitudinal axis. The system includes an image acquisition assembly, a line light assembly, and a computing unit. The image acquisition assembly has a field of view configured to image a first predetermined width over a circumference of a surface of the bar to define an image belt. The image acquisition assembly is further configured to produce image data corresponding to the acquired image belt.

The line light assembly is configured to project a light line belt having a second predetermined width onto the surface of the bar. The light line assembly is disposed, for example by alignment, relative to the image acquisition assembly such that the image belt is within the light line belt. The light line assembly is further configured such that a light intensity is substantially uniform along the image belt when the light is collected by each of the image acquisition sensors.

For packaging purposes, the line light assembly may include a collection of reflecting elements such as mirrors to achieve the designed projection angle. For serviceability, the collection of the reflecting elements is designed to be detachable.

Finally, the computing unit is coupled to the image acquisition assembly and is configured to receive image data for a plurality of image belts acquired by the image acquisition assembly as the bar moves along the longitudinal axis. The computing unit is further configured to process the image data to detect predetermined surface features of the bar. In a preferred embodiment, the detected features are surface defects and the image acquisition assembly includes n digital cameras, where n is an integer 3 or greater, arranged so that a combined field of view of the cameras corresponds to the image belt.

A method of imaging a metal bar is also presented.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will now be described, by way of example, with reference to the accompanying drawings, wherein like reference numerals identify identical components in the several figures, in which:

FIG. 1 is a schematic and block diagram view of an embodiment of the present invention.

FIG. 2 are cross-sectional views of exemplary geometries for work pieces suitable for inspection by an embodiment according to the present invention.

FIG. 3 illustrates a cross-sectional geometry of a metal flat.

FIG. 4 is a diagrammatic view illustrating a conventional lighting scheme as applied to a metal flat and a bar.

FIG. 5 are simplified perspective views illustrating a bar constrained during its travel by a conduit, and a gap between adjacent conduits in which an embodiment according to the invention may be situated.

FIG. 6 is a simplified plan view illustrating an imaging coverage on a metal bar using one camera.

FIG. 7 is a simplified plan view illustrating an imaging coverage on a metal bar with one camera and a telecentric lens.

FIG. 8 is a simplified plan view illustrating an arc length variation based on a projection of same size grids, such as a line of pixels, onto a bar profile.

FIG. 9 is a simplified plan view illustrating a lighting arrangement for a bar surface in accordance with the present invention.

FIG. 10 is a simplified plan view further illustrating, in greater detail, the lighting arrangement of FIG. 9.

FIG. 11 is a simplified perspective view of a metal bar in connection with which the lighting arrangement of the present invention is used.

FIG. 12 is a simplified plan view illustrating the lighting arrangement in the circumferential direction as directed toward a bar surface.

FIG. 13A is a plan view illustrating another embodiment of a lighting and imaging arrangement for a bar surface according to the invention.

FIG. 13B is a diagrammatic view of the lighting arrangement of FIG. 13A such that the collection of reflective elements can be retrieved for cleaning and restored for function easily, as shown in an installed position.

FIG. 13C is a diagrammatic view of the lighting arrangement of FIG. 13B, including the collection of reflective elements, shown in a partially removed position.

FIG. 13D is a diagrammatic, perspective view of the embodiment of Figure 13B, showing a protective tube.

FIG. 13E is a diagrammatic, side view of the embodiment of FIG. 13B.

FIG. 13F is a diagrammatic, perspective view of the embodiment of FIG. 13B viewed from an opposite side relative to that in FIG. 13D.

FIG. 14A illustrates a surface defect along with some surface noise.

FIG. 14B illustrates an exemplary result of an image processing step according to the invention as applied to the image of FIG. 14A.

FIGS. 15A-15C illustrate examples of long surface defects that may be found on metal bars and which can be detected by an embodiment according to the present invention.

FIGS. 16A-16C illustrate relatively short surface defects that may be found on metal bars and which can be detected by an embodiment according to the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention permits automated inspection of metal bars for surface defects as the metal bars are being rolled, drawn or the like (i.e., the reducing process described in the Background of the Invention) without additional handling to the bars. FIG. 1 schematically illustrates a preferred embodiment in accordance with the present invention.

Before proceeding to a detailed description of the present invention keyed to the drawings, a general overview will be set forth. The present invention provides the following features:

1. Capable of working for metal bars manufactured through reducing processes at different cross section geometry;

2. Capable of working for metal bars in-line at a bar temperature up to 1,650° C.;

3. Capable of working for metal bars traveling at 100 m/s or higher;

4. Capable of detecting surface defects whose critical dimensions are as small as 0.025 mm;

5. Capable of reporting the defect nature such as its size, location (on the bar), image, and the like;

6. Capable of accommodating different sizes of bars, for example only, from 5 mm to 250 mm with minimum adjustment;

7. Capable of providing real-time or near real-time inspection results;

8. Capable of working with a small access window (less than 50 mm) to the target object;

9. No moving parts while inspecting;

10. No additional handling of the bars; and

11. Continuous operation in commercial, heavy industrial metal production mills.

FIG. 1 is a simplified schematic and block diagram of a system in accordance with the present invention. FIG. 1 shows line light assembly which may include at least one light source 2, a light conduit 4, a plurality of line lights 6 and a corresponding plurality of optical boosters 8. FIG. 1 further shows a computing unit 10 and an image acquisition assembly that may include a plurality of cameras 12 each having a corresponding lens 14.

With continued reference to FIG. 1, a workpiece or object under inspection, such as an elongated metal bar 16 extending along a longitudinal axis, is shown moving along its longitudinal direction 20 at a speed up to 100 m/s or faster while bar 16 is going through a reducing process. The metal bar 16 may be formed from one selected from the group comprising steel, stainless steel, aluminum, titanium, nickel, copper, bronze, or any other metal, and/or their alloys. The bar 16 may be solid or hollow. Typically such metal bar 16 is traveling inside a conduit, as shown in greater detail as conduit 24 in FIG. 5, not shown in FIG. 1. A gap 26, shown in FIG. 5, is defined between two adjacent conduits 24, and is typically very small, for example between about 20 to 50 mm taken in the axial direction for high-speed transit of metal bars 16. It should be understood that metal bar 16 may be at an elevated temperature, for example as hot as 1,100° C. for a hot rolling process. It should also be appreciated that metal bar 16, given its geometry, is prone to twist/rotate about its longitudinal axis uncontrollably in the direction indicated by arrow 21 in FIG. 1 when it travels in direction 20. This possibility for uncontrollable rotation has, among other items, presented problems for conventional imaging systems. As will be described in greater detail below, the present invention overcomes this problem to provide an imaging system that is robust to twisting and/or rotation.

In order to detect surface defects on bar 16, an imaging system in accordance with the present invention must be provided having certain features, as described below. With continued reference to FIG. 1, the imaging system includes an image acquisition assembly that preferably comprises n imaging cameras 12, wherein n is an integer 3 or greater. The parameter n is selected to be three or higher based on an analysis set forth below. Each camera 12 is arranged so as to cover a circumferential span of at least 120° in order to image the entire surface of bar 16. That is, the image acquisition assembly has a composite or combined field of view configured to image the entire circumference of the surface of the bar 16 to define an image belt 18. As further described below, the image acquisition assembly is further configured to produce image data based on the image belt 18. The analysis for the parameter n for the number of cameras will now be set forth.

As shown in FIG. 6, a regular lens 14 associated with camera 12 will have a viewing angle (field of view) formed by the two tangential lines of sight 28 extending from a focal point of lens 14 to the surface of bar 16. This viewing angle, when projected onto a non-flat surface, such as the one shown in FIG. 6, will result in a circumferential coverage 30 that is less than 180° and will be insufficient to cover 360° with only two lens/camera units where the lens are not telecentric.

FIG. 7 shows an arrangement with a telecentric lens 14′. A true telecentric lens, which collects lines of sight that are in parallel, even if used, would not practically provide for a two-lens/camera system because of arc length variation. In particular, the lines of sight 28 are parallel with the addition of telecentric lens 14′ to lens 14. In this case, the circumferential coverage 30 is 360°. Theoretically speaking, the entire surface of round shaped bar 16 can be covered using only two lens/camera units. However, as alluded to above, a problem of non-uniform pixel sizes arises.

As illustrated in FIG. 8, the evenly spaced lines of sight 34, as derived from an evenly-spaced imaging sensor 32 having a plurality of pixels, can result in an uneven arc length 36 on the surface of bar 16, pixel-to-pixel. Even spacing is a very typical arrangement on an imaging sensor such as a CCD chip. The arc length 36 can be calculated using equation (1) as follows:

S=p/ cos(θ)  EQN (1)

where S is the arc length 36 mapped to the pixel in position y, p is the pitch of the pixel array or the pixel size, and θ is the projected angle that can be derived from

θ=arc sin(y/r), in which y≦r and r is the radius of the metal bar 16.   EQN (2)

From FIG. 8 one can learn that as y→r, θ→90°. As θ→90°, S the arc length 36 will approach infinity based on EQN (1). In reality, S will still be a finite number. However, S will be substantially (several times) larger than p, the pixel size. That is, the image resolution in this area will deteriorate so much that this approach is infeasible. Note that the same arc length analysis can be applied to the bottom half in FIG. 8, in which case y→−r.

With three cameras, θ can be established at 60°. When θ=60°, S the arc length 36 (at the 12 o'clock and 6 o'clock positions in FIG. 8) is only 2p, an acceptable and controllable deterioration in image resolution. If better image resolution is desired, four cameras or five cameras, or even more may be used (i.e., the parameter n referred to above can be an integer equal to four, five or greater). All the lens 14/camera 12 combinations, as illustrated in FIG. 1, are preferably arranged such that all such lens/camera combinations are positioned along a circular path 22 that is concentric to the circular geometry of the exemplary metal bar 16 such that the working distances, the distance from each lens 14 to the nearest metal surface, are the same or nearly the same for all the lens/camera combinations. Note that the path 22 may stay circular if the metal bar is non-circular, say a hexagon, for the purpose of generally serving the same manufacturing line. One that is skilled in the art can appreciate that the path 22 can, if desired, be made to conform to the actual bar geometry.

In order to accommodate the potentially very high traveling speed of the metal bar 16, high data rate cameras 12 are preferably used. The cameras 12 in the system are thus preferably digital cameras, with digital outputs to computing unit 10. This digital output format is desirable to accommodate the harsh environment for signal fidelity. This digital format image signal may be received by the computing unit 10 through standard communication channels such as IEEE-1394 (also known as FireWire), Camera Link or USB ports, or a special interface known as a frame grabber. Each camera 12 preferably is able to generate at least 10,000,000 (or 10 Mega) pixels per second such that a defect feature that is 0.025 mm×0.5 mm can be identified. It should be appreciated, however, that to detect larger features, a reduced resolution, and hence reduced data rate (in pixels per second) would be required. Line scan cameras are preferred even though progressive (non-interlaced) area scan cameras can be used when the bar 16 is not traveling fast. Line scan cameras have an advantage over area scan cameras in that line scan cameras only require a line of illumination, instead of an area of illumination. This will simplify the illumination complexity caused by the non-flat surface. In the case of using line scans, all the cameras in FIG. 1 will be aligned such that their imaging lines will be forming a circumferential ring, an image belt 18, on bar 16. This alignment is necessary to address the issue of twist and/or rotation (item 21). If this alignment is not held, the twisting or rotating motion can result in incomplete coverage of the bar surface.

Referencing back to FIG. 1 again, each camera will have a lens 14 to collect light reflected from the bar surface. Telecentric lenses (lenses that collect parallel image light rays, as illustrated with FIG. 7) are preferred for a more uniform arc length distribution, even though regular lenses can be used. In addition, cameras 12 may be configured to include a lens iris to control exposure, and further, preferably configured (if included) with the use of a predetermined lens iris setting for improved depth of focus/field in the application.

With continued reference to FIG. 1, the imaging system according to the present invention also includes a line light assembly configured to project a light line belt onto the surface of the metal bar 16. Preferably, the line light assembly includes a plurality of line lights 6. These line lights 6 can be individual light sources, such as lasers, or light delivery devices, such as optical fiber lights, as shown in FIG. 1. The light delivery devices must work with at least one light source, as shown in FIG. 1. More than one light source can be used if higher light density is needed for illumination. For metal bars 16 that travel at very high speed, the cameras may be light starved due to very high line/frame rates equating to a relatively short exposure time. An optical booster 8 may therefore be used for each line light to concentrate the light and increase the light intensity. This booster 8 can be a cylindrical lens or a semi-cylindrical lens. To use the imaging system in accordance with the present invention for metal bars 16 that are at an elevated temperature, the line lights and the boosters must be made of special materials configured to withstand such elevated temperatures. Each line light 6, for example, may be configured to have its own glass window to serve this purpose. In the case of optical fiber line light, the material that binds the fibers together must be able to withstand high temperature, such as the high temperature epoxy. The boosters 8 must be made of materials that can withstand high temperature, too. Usable materials include glass, Pyrex, crystal, sapphire, and the like.

FIG. 9 is a top view of the preferred embodiment shown in FIG. 1. To cope with light starving, the alignment between the line lights and the cameras is important. As illustrated in FIG. 9, the surface of metal bar 16 after the reducing process, before, for example, a descaling process, can be treated as a reflective surface. Therefore, the optical law set forth in equation (3) applies:

“incident angle=reflective angle”  EQN (3)

EQN (3) is preferably used in a preferred embodiment to maximize the reflected light that is captured by the plurality of cameras 12. The line lights 6 will each emit the light ray 40, which is boosted by a booster 8 and projected onto the surface of the metal bar 16. The light ray 40 is reflected to the path 42 and received by the lens 14 and eventually by the camera 12. Note that in FIG. 9, the metal bar 16 travels in the direction 20. The projected and reflected light rays 40 and 42 form an angle 44, equally divided by the normal line to the surface of the metal bar 16. This angle 44 must be as small as possible, due to the illumination problem described above that is associated with a non-flat surface, as illustrated in FIG. 4. In FIG. 4, the light line 18′ and the image line 18 will not overlap on a non-flat surface. The ideal case is for the angle 44 in FIG. 9 to be 0°. As this is only possible by using a beam splitter, it is less practical to do so when the system is light starving due to inherent power losses imposed by using a beam splitter for example. The highest efficiency a beam splitter can achieve is 25%, assuming a 0% transmission loss. Therefore, the angle 44 is preferably selected so as to be reasonably small, such as 1° or in its neighborhood. If necessary, a reflective mirror 38 can be used to assist in packing the camera and the light for a small angle 44. This is another reason to use line scan cameras in this application. Line scan cameras only need an image path 42 with a small width, such as from 5 to 30 microns. The angle 44 can be kept very small with this small image path feature.

FIG. 10 shows in greater detail a portion of the lighting setup of FIG. 9. As mentioned above, the angle 44 will not be 0 degrees unless a beam splitter is used. Therefore, each line light 6 must have a substantial width W (item 41 in FIG. 10). One can see that in FIG. 10 the metal bar 16 has a centerline 46. The line 48 indicates the 60° mark on the bar surface, starting from the tangential boundary on the left hand side of the bar, as shown in FIG. 10, and increasing to the right. One camera must be able to image the metal bar 16 for the upper half to this 60° mark line 48. In a three-camera embodiment, the above calculations apply. If more cameras are used, the line 48 may represent 45° for a four-camera system, at 36° for a five-camera system, and so forth. If designed symmetrically, the camera can also image the bottom half of the metal bar 16 for 60°. In order to achieve this coverage, the light line width W must be greater than a threshold based on:

W≧2·r·(1−cos 60°)·sin α  EQN (4)

in which r is the bar radius and α is the incident angle (half of the angle 44). The 60° can be replaced by another angle if a different numbers of cameras other than three are used in the inventive imaging system. This notion is further illustrated in FIG. 11, in which the image line 42 is clearly curved differently, yet covered by the light line 40. In other words, the image acquisition assembly (e.g., the plurality of cameras in the preferred embodiment) captures an image belt 18 having a first predetermined width over the entire circumference of the surface of the bar 16. The line light assembly (e.g., the plurality of line light sources in the preferred embodiment) projects a light line belt onto the surface of the bar 16 having a second predetermined width. The line light assembly is disposed and aligned relative to the image acquisition assembly such the image belt falls within the light line belt. Through the foregoing, the problem of non-flat surfaces is overcome.

Additionally, these line lights must be positioned such that the light intensity as reflected from a point on the bar surface to the camera that covers that point is uniform for all the points on the image belt 18 (FIG. 1). A more detailed illustration is shown in FIG. 12. All the illumination must follow the law described in EQN (3). FIG. 12 illustrates this arrangement for one camera. It should be appreciate that such arrangement may be duplicated for other cameras used in the inventive imaging system. Based on EQN (3), the angle formed by the incident light ray 40 and the reflected light ray 42 must be evenly divided by the surface normal 50. As in FIG. 12, an illuminator 52 preferably includes a curved surface. Illuminator 52 is a device whose emitted light rays (perpendicular to this curved surface at the point of emission) will be reflected by the surface of the bar 16 to the imaging sensor in camera 12 and lens 14 based on EQN (3). Note that curve 52 need not be a circular curve. This curve 52 depends on the distance between the curve 52 and the surface of the bar 16 (i.e., target). Curve 52 may not be a smooth curve if the bar is not circular. Even though an illuminator with curve 52 can be made with modern technologies, such illuminator can only be used with bars 16 at the designated diameter. In some applications it is not practical. An alternative is to simulate such illumination effect with an array of light lines 6 and 8, as shown in FIG. 12. Each combination of light line/booster can be made adjustable such that its direction can be re-pointed as shown by item 54 to accommodate targets with different diameters. The light line approach is also beneficial in the case that the bar 16 is not circular.

FIG. 13A is a simplified schematic and block diagram view of another embodiment of a system in accordance with the present invention. This embodiment provides a very easily serviceable cassette containing reflective elements that are packaged in a relatively small space (e.g., 20 to 50 mm) so as to be operable in the small access gap 26 (best shown in FIG. 5) with the workpiece/moving bar 16 being contained and longitudinally moving in direction 20 through conduit 24 or the like. FIG. 13A shows line light assembly 6, optical booster 8, camera 12, lens 14, reflective mirror 38 for the incident/illuminated light ray 40, a second reflective mirror 38′ for the reflected (image) light ray 42 representing the image of the bar surface, and a protection device such as a tube 43 having a first part 43 a and a second part 43 b spaced apart and offset from the first part 43 a along axis “A” to define an access space 43 c. The protection parts 43 a, 43 b are configured to protect the relatively fragile imaging and illumination components from the heat, shock (e.g., contact) and other contamination (e.g., particles) originating from moving bar 16, which may be at an elevated temperature (as described above). Parts 43 a and 43 b may be circumferential. Aperture 43 c may be configured in size and shape to allow entry/exit of illumination light rays 40 and reflected (image) light rays 42. Protection tube 43 may be formed of metal or other durable material suitable for segregating hot steel bar 16 from the rest of the inventive system.

FIG. 13A further shows a contamination reduction mechanism, employing a vacuum, which is configured to reduce the presence of airborne, relatively small size contaminants 62, such as mill scale powder or tiny water mist, that may be present in the space proximate or near the access space 43 c of the protection tube 43 (i.e., contaminants that are emanating from the moving metal bar in the interior of the protection tube). This contaminant reduction mechanism may operate in combination with air knives or air wipes or the like in and around access 43 c, which are configured to block larger items from fully exiting access space 43 c. One advantage of the vacuum-based contaminant reduction mechanism is that it keeps the optical components relatively contaminant free, or at a reduced contaminant level, thereby keeping them cleaner and improving optical performance (i.e., compared to dirty optical components). Additionally, this contamination reduction mechanism may be operative to reduce airborne contaminants in the imaging path, which may improve visibility of the image acquisition means.

The contaminant reduction mechanism includes a vacuum end effector 64 having a vacuum connector 66, a pipe or other vacuum conduit 66′ having a first end configured to connect to the connector 66, and a source of vacuum such as vacuum pump 72, which is coupled to the other end of conduit 66′.

The vacuum end effector 64 is preferably in a ring shape, as shown in the figures, and is formed about a ring axis and having a vacuum suction inlet 70 circumscribing the space in and around the access space 43 c of protection tube 43. As installed, the ring axis of the end effector 64 is substantially coincident with the longitudinal axis along which the metal bar moves. End effector 64 is of thin-wall construction and of a generally closed geometry whose plurality of contiguous, outer thin-wall sides define an interior vacuum chamber 68. In the preferred embodiment, the ring shaped vacuum end effector 64 is characterized by a rectangular shape in radial cross-section (best shown in FIG. 13E). It should be understood, however, that the vacuum end effector 64 may take various shapes, for example, a pair of half-rings arranged in cooperating fashion to provide vacuum coverage around the perimeter of access space 43 c. Additionally, vacuum end effector 64 may take the form of a plurality of straight bars arranged around the perimeter of access space 43 c. Other variations are possible, which are within the spirit and the scope of the present invention.

The vacuum source (pump 72) operates through the conduit 66′, vacuum chamber 68, and finally via suction inlet 70 to apply vacuum (and thus substantially evacuate) the space proximate the access space 43 c. including any small, airborne contaminants 62.

FIG. 13B is a diagrammatic front perspective view showing a plurality of reflective mirrors 38 (illumination directing) configured in a removable cassette 152. FIG. 13B shows eight reflective mirrors 38 supported by a corresponding number of mirror seats 138. Cassette 152 is removable and is shown in the installed position (FIG. 13B) and in a nearly, fully removed position (best shown in FIG. 13C). Cassette 152 is shown mounted onto a holder such as a plate 150. Plate 150 can be linked to other elements of the inventive imaging system through a base plate 154.

In the illustrative embodiment, plate 150 is configured to include a sliding groove 156 around an inner perimeter of plate 150. Cassette 152 includes a plurality of fitting tabs 158 (four shown arranged in diametrically opposed pairs) configured in size and shape to mate with groove 156. The dimensional tolerance is such that cassette 152, particularly the mirrors 38 thereof, will be properly aligned with components 14/12 and components 6/8 when cassette 152 is in the installed position. It should be appreciated that cassette 152 includes the passive components, namely, illumination directing mirrors 38 and image reflecting mirrors 38′ (best shown in FIGS. 13E and 13F), and thus does not require any connections via cables, power wires or the like to other elements external to cassette 152 that comprise the inventive illumination and imaging system. This provides an advantage inasmuch as the cassette 152 may be removed for cleaning and reinstalled relatively easily due to the absence of such connections.

Cassette 152 may be maintained in the installed position (i.e., in alignment) through the use of a suitable locking and retention mechanism, such as a simple closure member 153 (shown in phantom line in FIG. 13B), having suitable mating features to also slide in groove 156, and be retained therein (e.g., fasteners). One of ordinary skill in the art will appreciate that there are a wide variety of alternate suitable locking and retention mechanisms.

In the embodiment of FIG. 13B, four cameras 12 are used.

FIG. 13B further shows the ring embodiment of the contaminant reduction mechanism in perspective view.

FIG. 13C is a simplified diagrammatic view of cassette 152 in the removed position. Cassette 152 can be easily removed by first defeating/disabling any locking and retention mechanism 152 that may be in-use, and removing the cassette in the direction of arrow 160, for example, for servicing (e.g., cleaning, repair, re-alignment). The cassette 152 may be remounted/reinstalled easily by reversing the above-described procedure.

FIG. 13D is a diagrammatic, front perspective view of the embodiment of FIG. 13B showing a tube-shaped protection device 43 a and 43 b. FIG. 13D also shows locking and retention mechanism 153 in the installed, locked position. In the installed position as shown, the illumination directing mirrors 38 and the image directing mirrors 38′ are in alignment with the light line assembly (light source 6 and booster 8) and lens 14/camera 12, respectively.

FIG. 13D further shows vacuum end effector 64, as taken in radial cross-section through the middle (half of the ring omitted for clarity). As shown, the end effector 64 includes a plurality of thin-wall sides defining the interior vacuum chamber 68. Suction inlet 70 is also shown, which may be formed by removing a radially inwardly facing corner to reveal the suction inlet 70.

FIG. 13E is a diagrammatic, side view of the embodiment of FIG. 13B, with the cassette 152 in the installed position. FIG. 13E shows image directing mirrors 38′ in alignment with lens 14 and camera 12. FIG. 13E also shows the camera viewing gap 43 c defined in between protection tube portions 43 a and 43 b.

FIG. 13E further shows a side view of the cross-sectioned vacuum end effector 64 of FIG. 13D. FIG. 13E shows as a side plan view the interior vacuum chamber 68 and the vacuum suction inlet 70. Inlet 70 faces generally radially inwardly toward, as well as circumscribing the perimeter of the access space 43 c.

Vacuum end effector 64 may be formed using conventional construction techniques and materials (e.g., metal or other durable materials). Vacuum connector 66 and conduit 66′ may also comprise conventional construction techniques and materials known to those of ordinary skill in the art. Additionally, the vacuum pump 72 may also comprise conventional apparatus known to those of ordinary skill in the art. For example, the vacuum pump 72 may be a venturi or electrical type or other type known in the art.

The desired, preselected applied vacuum level (i.e., level of vacuum as observed at suction inlet 70) may be determined by the particular degree, presence and type of small contaminants 62, and the geometry of, orientation and proximity of suction inlet 70 with respect to access space 43 c. The corresponding performance characteristics of vacuum pump 72 may be determined based on the above determined applied vacuum level desired, in view of the particular geometry and size/volume of end effector 64, as well as the size and length of connector 66 and conduit 66′.

FIG. 13F is a diagrammatic rear perspective view of the embodiment of FIG. 13B. FIG. 13F shows three image directing mirrors 38′ in cassette 152 (one mirror 38′ for each lens 14/camera 12 combination). Note, one mirror 38′ is obscured in FIG. 13F, as is the corresponding lens 14/camera 12 combination.

Referencing back to FIG. 1, a computing unit 10 is coupled to plurality of cameras 12. The computing unit 10 is configured to receive the image data for a plurality of image belts 18 acquired successively by the cameras 12 as the bar 16 moves along the longitudinal axis in the direction 20 (direction 20 best shown in FIG. 1). Frame grabbers may be used to receive the image signals. The cameras 12 in the system, however, are preferably digital cameras, as described above. The computing unit may comprise one or more computers in order to have enough computing power to process the image data. Image processing hardware may be used in conjunction with the software for faster computing speed. If multiple computers are used, these computers can be linked together through inter-computer links such as TCP/IP or the like.

In any event, computing unit 10 is configured to process the image data to detect predetermined features of the surface of bar 16. In a preferred embodiment, the features are surface defects. Thus, the image data will be processed for defects, such defects being shown in exemplary fashion in FIGS. 14A-14B. The images typically contain both the real defects (e.g., item 302) and noise, such as scratch marks (e.g., item 304). Image processing algorithms, implemented in computer codes such as C, C++, machine languages, and the like, or implemented in hardware logic, are used to filter out the noise, and to detect the true defects, as shown in 306. The defects to be identified can be long and have a large aspect ratio, as shown in FIGS. 15A-15C, where item 308 may be 1000 mm long, and item 310 may indicate a width of 0.050 mm. Or, the defects can be short and have a nearly 1-to-1 aspect ratio, as shown in FIGS. 16A-16C. These algorithms are known in the art, but will be described generally. A first layer of processing may involve a comparison of local contrast in the image, such as by comparing a first predetermined threshold to the local contrast. A second layer of processing may involve applying a second predetermined threshold to detect the nature of the defect such as size, location, length and width and the like.

The preferred embodiment described and illustrated in connection with FIG. 1 will also have protection against dust, water, vibrations, and other damaging factors in a typical metal process plant such as a hot rolling mill or a cold drawing mill.

Those skilled in the art shall appreciate the possibility of further restrain the bar and separately using three or more single-camera systems in the reducing process line for inspection.

Those skilled in the art shall also appreciate that covering (e.g., inspection of ) a portion of the bar surface less than the entire circumference may be useful enough for statistical process control purpose in the reducing process line.

Those skilled in the art shall also understand that a very high speed (high data rate and high frame rate) area scan camera can be used in place of the line scan cameras if only a certain portion of each of the area scan images is used for processing.

One can also understand that if the metal bars are at an elevated temperature, an optical filter can be used in conjunction with the lens such that only certain wavelengths in the reflected light rays 42 (in FIG. 12) will be used to carry the surface information of the metal bars. Such wavelengths are those not emitted or not dominantly emitted by the metal bars at the said elevated temperature. For metal bars at or colder than 1,650° C., the wavelength 436 nm can be used. In this case, an interference filter at 436 nm will be used with the lens. This wavelength can vary with the temperature. If the temperature decreases, longer wavelength can be used.

In a still further variation, the light line assembly may be configured to include a strobe light, wherein the computing unit 10 synchronizes the illumination (i.e., the strobing) with the image capture function performed by the image acquisition assembly (e.g., the cameras 12 in the preferred embodiment).

In a yet still further embodiment, the computing unit 10 is configured to maintain a running record of the detected defects, including (i) a respective location of each detected defect relative to a “start” position, such as the leading end, on the bar 16 being manufactured through processes that mechanically reduce the cross-sectional area of the metal bars; (ii) a respective notation of the nature of the detected defect, such as the size, shape, contrast; and (iii) optionally, an actual image of the site of and surrounding the detected defect. The record may be useful to the supplier/manufacturer, for example, for determining an up-front discount, and may be provided to the customer (e.g., on a diskette or other electronic means) for use in further processing, for example, what portions of the bar to avoid or do follow-up work on. 

1. A system for imaging an elongated bar extending and moving along a longitudinal axis in a manufacturing process, said system comprising: an image acquisition assembly having a field of view configured to image a first predetermined width over a circumference of a surface of said bar while said bar is moving to define an image belt and produce image data corresponding thereto, said image acquisition assembly including n digital line scan cameras, where n is an integer 3 or greater, arranged so that a combined field of view thereof corresponds to said image belt; a light assembly configured to project light onto the surface of said bar such that a light intensity on the bar surface is substantially uniform along said image belt; and a computing unit coupled to said image acquisition assembly configured to receive image data for a plurality of image belts acquired by said image acquisition assembly as said bar moves along said longitudinal axis, said computing unit being further configured to process said image data to detect predetermined surface features of said bar.
 2. The system of claim 1 wherein said light from said light assembly forms a light line belt having a second predetermined width and having said substantially uniform light intensity at said bar surface, said image belt being within said light line belt.
 3. The system of claim 1 wherein said coupling between said image acquisition assembly and said computing unit comprises at least one of a digital format frame grabber, an IEEE-1394 channel, a USB port, and a Camera Link port.
 4. The system of claim 1 wherein said image acquisition assembly further includes optical filters intermediate said cameras and said bar configured to selectively allow predetermined wavelengths to reach said cameras such that said features of said bar are not obscured when said bar is at or higher than a predetermined temperature at which said bar self-emits a characteristic electromagnetic radiation (EMR) spectrum.
 5. The system of claim 1 wherein said light assembly comprises a plurality of line light sources.
 6. The system of claim 1 wherein said light assembly includes an illuminator comprising optical fibers arranged to deliver light generated from one or more light sources.
 7. The system of claim 6 wherein said line light sources comprise lasers with line generating optics associated therewith.
 8. The system of claim 6 wherein said light assembly further includes a plurality of optical boosters for use with said light line sources configured to increase an illuminating light intensity.
 9. The system of claim 1 wherein said detected features include surface defects.
 10. The system of claim 1 wherein said computing unit is configured to maintain a record of said detected defects including a respective location of each detected defect relative to a start location of said bar.
 11. The system of claim 10 wherein said record further includes a respective notation as to the nature of each detected defect including at least one of a size, a shape and a contrast level of each detected defect.
 12. The system of claim 10 wherein said bar is formed of metal manufactured through a process that mechanically reduces a cross-section area of said bar.
 13. The system of claim 1 wherein said computing unit comprises a plurality of computers.
 14. The system of claim 1 wherein said computing unit includes at least one of (i) a first hardware unit that embeds a computing process or instructions, such as an ASIC and/or FPGA; (ii) a second hardware unit that executes software codes, such as a CPU and/or a DSP; and (iii) a combination of said first and said second hardware unit.
 15. The system of claim 9 wherein said computing unit is configured to differentiate said surface defects from surface noises.
 16. The system of claim 12 where said metal bar has a cross-sectional area associated therewith, said metal bar having a ratio of said circumference to said cross-sectional area that is less than or equal to 4.25 when the cross-sectional area is unity for a shape selected from the group comprising a round shape, an oval shape, and a polygonal shape.
 17. The system of claim 16 wherein said metal bar is at an elevated temperature up to 1,650° C.
 18. The system of claim 16 wherein said metal bar is formed from one selected from the group comprising steel, stainless steel, aluminum, titanium, nickel, copper, bronze, or any other metal, and/or their alloys.
 19. The system of claim 16 wherein said metal bar is hollow.
 20. The system of claim 10 wherein said image data is suitable for statistical process control (SPC) purposes.
 21. The system of claim 4 wherein said wavelengths comprise a 436 nm wavelength when a temperature of said bar is at or below 1,650° C.
 22. The system of claim 6 comprising materials that can withstand high temperature such as high temperature epoxy and glass fibers.
 23. The system of claim 8 wherein said optical boosters comprise cylindrical and/or semi-cylindrical lenses made of glass material selected from the group comprising fused silica, Pyrex, and sapphire.
 24. The system of claim 1 wherein said light assembly includes a plurality of line light sources each projecting light beams at a first predetermined angle relative to a normal line from the surface of the bar onto which said light beams impinge, and wherein respective principal axes of said cameras are disposed at a second predetermined angle relative to said normal line, said first and second predetermined angles being equal.
 25. The system of claim 24 wherein said first and second predetermined angles are about one degree.
 26. The system of claim 1 wherein said computing unit is configured to process a plurality of image belts defining said image data to detect predetermined surface features spanning multiple image belts of said bar.
 27. The system of claim 1 wherein said predetermined surface features include surface defects, said computing unit being further configured to maintain a record of said detected defects including (i) a respective location of each detected defect relative to a start location of said bar; (ii) a respective notation as to the nature of the detected defect selected from the group comprising a size, a shape and a contrast level; and (iii) an actual image of a site on said bar surrounding the detected defect.
 28. The system of claim 1 further comprising a removable cassette having an installed position and a removed position relative to a holder for said cassette, said cassette including (i) illumination directing mirrors intermediate a plurality of light sources and said bar, and (ii) image directing mirrors intermediate said bar and said cameras, said illumination mirrors and said image directing mirrors being in alignment when said cassette is in said installed position.
 29. The system of claim 28 further comprising a locking and retention mechanism configured to retain said cassette in said installed position.
 30. The system of claim 2 further comprising: a protection device comprising a tube having a first part and a second part spaced apart and offset from said first part along said longitudinal axis to define an access space, said tube being disposed intermediate the elongated bar and said image acquisition means and said light assembly, said access space being configured in size and shape to allow (i) entry of said light which forms said light line belt and (ii) imaging of said image belt, wherein said illumination directing mirrors and said image directing mirrors are disposed in said access space, and wherein said light assembly is protected from said bar by one of said first part and said second part of said protection tube, said image acquisition assembly being protected from said bar by one of said first part and said second part of said protection tube.
 31. The system of claim 30 wherein said tube comprises metal.
 32. The system of claim 30 further comprising: a contaminant reduction mechanism configured to reduce the presence of contaminants in the space proximate said access space of said protection tube.
 33. The system of claim 32 wherein said contaminants comprise one of mill scale powder and water mist.
 34. The system of claim 32 wherein said contaminant reduction mechanism comprises a vacuum end effector having an outer wall defining an interior vacuum chamber, said end effector further including a suction inlet located proximate said access space of said protection device, said vacuum end effector being configured to be connected to a vacuum source.
 35. The system of claim 34 wherein said vacuum end effector is a ring shape having a ring axis that is substantially coincident with said longitudinal axis, said suction inlet being configured in size and shape to circumscribe the perimeter of said access space.
 36. The system of claim 35 wherein said vacuum end effector is substantially rectangular in radial cross-section, said suction inlet being formed by removal of a radially-inward corner of said vacuum end effector.
 37. The system of claim 34 wherein said vacuum end effector comprises a pair of half-ring shape body portions.
 38. The system of claim 34 wherein said vacuum end effector comprises a plurality of straight bars.
 39. The system of claim 34 wherein said contaminant reduction mechanism further includes a conduit for connecting said source of vacuum to said vacuum end effector, said source of vacuum comprising a vacuum pump.
 40. The system of claim 39 wherein said vacuum pump is a venturi type.
 41. A method of imaging a bar moving and extending along a longitudinal axis, said method comprising the steps of: (A) forming a light line belt having a first predetermined width over a circumference or part of the circumference thereof on a surface the bar moving in the direction of the longitudinal axis wherein said light line belt is of substantially uniform light intensity; (B) capturing, using a plurality of digital line scan cameras, an image belt having a second predetermined width located within the light line belt in the process of movement of the bar wherein the second predetermined width corresponds to a line scan of the line scan cameras; (C) repeating steps (A) and (B) to obtain an image of a surface area of the metal bar; (D) analyzing the image for features in accordance with predefined criteria.
 42. The method of claim 41 wherein said forming step includes the substeps of: defining a normal line from the surface of the metal bar at the light line belt; determining an angle relative to the normal line; and projecting light beams at the determined angle relative to the normal line to thereby form the light line belt.
 43. The method of claim 42 wherein said capturing step includes the substeps of: disposing an image acquisition assembly so that a principal axis of image acquisition is equal to the determined angle.
 44. A combination product comprising: (i) a steel bar that has been inspected for surface defects by an inspection apparatus, and (ii) a record in electronic form created by the inspection apparatus describing the results of the inspection of said steel bar, said record including, for each detected defect: a respective location of each detected defect relative to a start position on the bar; a respective notation of the nature of the detected defect, such as the size, shape, contrast; and wherein said inspection apparatus is configured for imaging said bar wherein said bar is elongated and extends and moves along a longitudinal axis in a manufacturing process, said inspection apparatus including: an image acquisition assembly having a field of view configured to image a first predetermined width over a circumference of a surface of said bar while said bar is moving to define an image belt and produce image data corresponding thereto, said image acquisition assembly including n digital line scan cameras, where n is an integer 3 or greater, arranged so that a combined field of view thereof corresponds to said image belt; a light assembly configured to project light onto the surface of said bar such that a light intensity on the bar surface is substantially uniform along said image belt; and a computing unit coupled to said image acquisition assembly configured to receive image data for a plurality of image belts acquired by said image acquisition assembly as said bar moves along said longitudinal axis, said computing unit being further configured to process said image data to detect predetermined surface features of said bar, said computing unit being configured to generate said record.
 45. The product of claim 44 wherein said light from said light assembly forms a light line belt having a second predetermined width and having said substantially uniform light intensity at said bar surface, said image belt being within said light line belt.
 46. The product of claim 44 wherein said record further includes an actual image of the site of and surrounding the detected defect.
 47. The product of claim 44 wherein said record is configured for use by a customer of said product. 